OK ARISTOROD 12.50

OK Aristorod 12.50 is a bare Mn-Si-alloyed G3Si1/ER70S-6 solid wire for the GMAW of non-alloyed steels, as used in general construction, automotive components, pressure vessel fabrication and shipbuilding. OK Aristorod 12.50 is treated with ESAB’s unique Advanced Surface Characteristics (ASC) technology, taking MAG welding operations to new levels of performance and all-round efficiency, especially in robotic and mechanised welding. Characteristic features include excellent start properties; trouble-free feeding at high wire speeds and lengthy feed distances; a very stable arc at high welding currents; extremely low levels of spatter; low fume emission; reduced contact tip wear and improved protection against corrosion of the wire.

SKU: ER70S-6-1 Category: MIG/MAG Welding Wires

Description

Typical Tensile Properties

AWS CO₂ (C1) *As welded*
Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
30 %	530 MPa	430 MPa	–	–
EN 80Ar/20CO₂ (M21) *As welded*
Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
26 %	560 MPa	470 MPa	–	–
EN 80Ar/20CO₂ (M21) *Stress relieved*
Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
28 %	495 MPa	370 MPa	620 °C	15 hr
EN CO₂ (C1) *As welded*
Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
25 %	540 MPa	440 MPa	–	–

Charpy V-Notch Properties

AWS CO₂ (C1) *As welded*
Impact Value	Testing Temperature	Stress Relieved Testing Temp	Stress Relieved Testing Time
75 J	-30 °C	–	–
EN 80Ar/20CO₂ (M21) *As welded*
Impact Value	Testing Temperature	Stress Relieved Testing Temp	Stress Relieved Testing Time
130 J	20 °C	–	–
120 J	-20 °C	–	–
100 J	-30 °C	–	–
90 J	-40 °C	–	–
EN 80Ar/20CO₂ (M21) *Stress relieved*
Impact Value	Testing Temperature	Stress Relieved Testing Temp	Stress Relieved Testing Time
120 J	20 °C	620 °C	15 hr
90 J	-20 °C	620 °C	15 hr
EN CO₂ (C1) *As welded*
Impact Value	Testing Temperature	Stress Relieved Testing Temp	Stress Relieved Testing Time
110 J	20 °C	–	–
75 J	-30 °C	–	–

Weld Metal Analysis

*CO₂ (C1)*
Mn	C	Si	Ti+Zr
–	–	–	<0,01 %
*80Ar/20CO₂ (M21)*
Mn	C	Si	Ti+Zr
–	–	–	<0,01 %
1.46 %	0.08 %	0.85 %	–

Deposition Data

Diameter	Current	Deposition Rate	Voltage	Wire Feed Speed
1.0 mm	80-300 A	1.0-5.5 kg/h	18-32 V	2.7-15 m/min
1.32 mm	130-400 A	1.5-8.5 kg/h	19-35 V	2.4-15 m/min
1.4 mm	150-420 A	1.6-8.7 kg/h	22-36 V	2.3-12 m/min
1.2 mm	120-380 A	1.3-8.0 kg/h	18-35 V	2.5-15 m/min
1.6 mm	225-550 A	2.1-9.4 kg/h	28-38 V	2.3-10 m/min
1.14 mm	100-350 A	1.2-7.0 kg/h	18-34 V	2.6-15 m/min
0.8 mm	60-200 A	0.8-2.3 kg/h	18-24 V	3.2-10 m/min
2.0 mm	300-650 A	4.4-10.2 kg/h	32-44 V	3.0-7 m/min
0.9 mm	70-250 A	0.9-3.5 kg/h	18-26 V	3.0-12 m/min

Approvals:	ABS, 3Y SA, BV, SA3YM, CE, EN 13479, DB, 42.039.29, DNV-GL, III YMS, LR, 3YS H15, PRS, 3YS, RS, 3Y40MS, VdTÜV, 10052, CWB, B-G 49A 3 C1 S6 (B-G 49A 3 C G6), PV,ZG, JIS, YGW12 (C1), ZG, NAKS/HAKC, 1.0-1.6 mm, PV, NAKS/HAKC, 1.2-1.6 mm, ZG, RINA, 3Y S, ZG, RINA, 3Y S, PV
Classifications:	EN ISO 14341-A, G 38 3 C1 3Si1, Weld Metal, EN ISO 14341-A, G 42 4 M20 3Si1, Weld Metal, EN ISO 14341-A, G 42 4 M21 3Si1, Weld Metal, EN ISO 14341-A, G 3Si1, Wire Electrode, SFA/AWS A5.18, ER70S-6, Wire Electrode, CAN/CSA-ISO 14341, B-G 49A 3 C1 S6, Wire Electrode, JIS Z 3312, YGW 12 (C1), Wire Electrode

Approvals are based on factory location. Please contact ESAB for more information.

Alloy Type:

Carbon-manganese steel (Mn/Si-alloyed)